R03S (01005) S-Series, Low ESR Capacitor Multi-Layer High-Q Capacitors

Specifications

Electrical Specifications
Case Size:	01005
Capacitance:	0.2 - 10 pF

Mechanical Characteristics
Size	Units	Length	Width	Thickness	End Band
01005	In	.016 ± .001	.008 ± .001	.008 ± .001	.006 Max.

Mechanical Specifications
	Specification	Test Parameters
Solderability:	Solder coverage = 90% of metalized areas No termination degradation	Preheat chip to 120°-150°C for 60 sec., dip terminals in rosin flux then dip in Sn62 solder @ 240°±5°C for 5±1 sec
Resistance to Soldering Heat:	No mechanical damage Capacitance change: ±2.5% or 0.25pF Q>500 I.R. >10 G Ohms Breakdown voltage: 2.5 x WVDC	Preheat device to 80°-100°C for 60 sec. followed by 150°-180°C for 60 sec. Dip in 260°±5°C solder for 10±1 sec. Measure after 24±2 hour cooling period
Terminal Adhesion:	Termination should not pull off.	Linear pull force* exerted on axial leads soldered to each terminal. *0402 = 2.0lbs, 0603 = 2.0lbs (min.)
PCB Deflection:	No mechanical damage. Capacitance change: 2% or 0.5pF Max	Glass epoxy PCB: 0.5 mm deflection

Environmental Specifications
	Specification	Test Parameters
Life test:	No mechanical damage. Capacitance change: ±3.0% or 0.3 pF Q>500 I.R. >1 G Ohms Breakdown voltage: 2.5 x WVDC	Applied voltage: 200% rated voltage, 50 mA max. Temperature: 125°±3°C Test time: 1000+48-0 hours
Thermal Cycle:	No mechanical damage. Capacitance change: ±2.5% or 0.25pF Q>2000 I.R. >10 G Ohms	5 cycles of: 30±3 minutes @ -55°+0/-3°C, 2-3 min. @ 25°C, 30±3 min. @ +125°+3/-0°C, 2-3 min. @ 25°C Measure after 24±2 hour cooling period
Humidity, Steady State:	No mechanical damage. Capacitance change: ±5.0% or 0.50pF max. Q>300 I.R. = 1 G-Ohmbr /> Breakdown voltage: 2.5 x WVDC	Relative humidity: 90-95% Temperature: 40°±2°C Test time: 500 +12/-0 Hours Measure after 24±2 hour cooling period
Humidity, Low Voltage:	No mechanical damage. Capacitance change: ±5.0% or 0.50pF max. Q>300 I.R. = 1 G-Ohm min. Breakdown voltage: 2.5 x WVDC	Applied voltage: 1.5 VDC, 50 mA max. Relative humidity: 85±2% Temperature: 40°±2°C Test time: 240 +12/-0 Hours Measure after 24±2 hour cooling period
Vibration:	No mechanical damage. Capacitance change: ±2.5% or 0.25pF Q>1000 I.R. = 10 G-Ohm Breakdown voltage: 2.5 x WVDC	Cycle performed for 2 hours in each of three perpendicular directions. Frequency range 10Hz to 55 Hz to 10 Hz traversed in 1 minute. Harmonic motion amplitude: 1.5mm.

Capacitance Values*
Value (pF)	Cap Code	Tolerances	Value (pF)	Cap Code	Tolerances
0.2	OR2	A, B, C, D	2.4	2R4	A, B, C, D
0.3	OR3	A, B, C, D	2.7	2R7	A, B, C, D
0.4	OR4	A, B, C, D	3.0	3R0	A, B, C, D
0.5	OR5	A, B, C, D	3.3	3R3	A, B, C, D
0.6	OR6	A, B, C, D	3.6	3R6	A, B, C, D
0.7	OR7	A, B, C, D	3.9	3R9	A, B, C, D
0.8	OR8	A, B, C, D	4.3	4R3	A, B, C, D
0.9	OR9	A, B, C, D	4.7	4R7	A, B, C, D
1.0	1R0	A, B, C, D	5.1	5R1	B, C, D
1.1	1R1	A, B, C, D	5.6	5R6	B, C, D
1.2	1R2	A, B, C, D	6.2	6R2	B, C, D
1.3	1R3	A, B, C, D	6.8	6R8	B, C, D
1.4	1R4	A, B, C, D	7.5	7R5	B, C, D
1.5	1R5	A, B, C, D	8.2	8R2	B, C, D
1.6	1R6	A, B, C, D	9.1	9R1	B, C, D
1.7	1R7	A, B, C, D	10	100	F, G, J, K
1.8	1R8	A, B, C, D	11	110	F, G, J, K
1.9	1R9	A, B, C, D	12	120	F, G, J, K
2.0	2R0	A, B, C, D	13	130	F, G, J, K
2.1	2R1	A, B, C, D	15	150	F, G, J, K
2.2	2R2	A, B, C, D	16	160	F, G, J, K
Custom Values Available - Contact Factory